Kusetshenziswa i-aluminium emsulwa njenge-matrix material, i-TiH2 njenge-ejenti egwetshwayo kanye ne-copper-plated glass fiber njengesengezo, i-aluminium enegwebu ene-porosity ehlukene yalungiswa. Umthelela wokuqukethwe kwe-fiber yengilazi kanye ne-aspect ratio ku-porosity, ukuminyana okubonakalayo, amandla acindezelayo kanye nokushisa okushisayo kwegwebu le-aluminium kwafundwa. Imiphumela ibonisa ukuthi uma inani le-ejenti eligwebu lihlala lingashintshiwe, ngokwanda kokuqukethwe kwe-fiber yengilazi kanye ne-aspect ratio, i-porosity ye-aluminium enegwebu iyanda, futhi ukuminyana okubonakalayo, ukuqhutshwa kwe-thermal namandla okucindezela kuyancishiswa ngokufanayo; kodwa ubude befiber Ithonya lesilinganiso sobubanzi lincane kunalelo lokuqukethwe kwefayibha.